UNS R30400 and T-400C Alloys: Product Introduction
UNS R30400 and T-400C, are cobalt-based superalloys known for their exceptional wear resistance and high temperature capabilities. This article provides a comprehensive introduction to these alloys, covering their chemical composition, mechanical properties, performance at different temperatures, industry applications, shapes and sizes, production standards, welding and processing capabilities, advantages and disadvantages, and comparisons with similar alloys.
Composition chimique
UNS R30400 and T-400C have similar chemical compositions, designed for superior wear resistance and mechanical strength:
| Élément | UNS R30400 (%) | T-400C (%) |
|---|---|---|
| Cobalt (Co) | 60.0 | 59,5 |
| Chrome (Cr) | 30.0 | 28.0 |
| Nickel (Ni) | 5.0 | 5.0 |
| Molybdène (Mo) | 5.0 | 5.0 |
| Carbone (C) | 00,15 maximum | 00,15 maximum |
| Silicium (Si) | 1,0 maximum | 1,0 maximum |
| Fer (Fe) | 2,0 maximum | 2,0 maximum |
Propriétés mécaniques
UNS R30400 and T-400C exhibit excellent mechanical properties suitable for high-wear applications:
| Propriété | États-Unis R30400 | T-400C |
|---|---|---|
| Résistance à la traction, ksi (MPa) | 200 (1380) minutes | 185 (1275) minutes |
| Limite d'élasticité (compensation de 0,2 %), ksi (MPa) | 140 (965) minutes | 130 (895) minutes |
| Allongement (% en 2 pouces) | 10 minutes | 10 minutes |
| Dureté, Rockwell C (HRC) | 40 – 48 | 38 – 46 |
Caractéristiques de performance
UNS R30400 and T-400C offer outstanding performance in harsh environments:
- Résistance à l'usure : Résistance exceptionnelle à l’usure adhésive, abrasive et érosive, ce qui les rend idéaux pour les composants soumis à des conditions d’usure élevées.
- Résistance à haute température : Conserve une résistance et une dureté élevées à des températures élevées, jusqu'à environ 1 000 °F (540 °C).
- Résistance à la corrosion : Bonne résistance à l’oxydation et à la corrosion dans divers environnements corrosifs, notamment les acides et les alcalis.
Applications industrielles
UNS R30400 and T-400C are utilized across various industries where wear resistance and reliability are critical:
| Secteur industriel | Applications |
|---|---|
| Automobile | Composants de soupapes, roulements de turbocompresseur et segments de piston dans les moteurs. |
| Aérospatial | Roulements, joints et composants de turbine dans les moteurs d'avion. |
| Pétrole et Gaz | Outils de forage, composants de pompe et sièges de vannes dans des environnements de forage agressifs. |
Formes et tailles
Ces alliages sont disponibles sous différentes formes et tailles pour répondre à différentes exigences d'application :
- Formes: Feuilles, plaques, barres, tubes et formes personnalisées.
- Tailles : Épaisseur allant de 0,025 pouces à 1,000 pouces (0,64 mm à 25,4 mm), diamètre allant de 0,25 pouces à 6,0 pouces (6,35 mm à 152,4 mm).
Normes de production
UNS R30400 and T-400C conform to industry standards ensuring quality and performance:
| Formulaire de produit | Formes disponibles | Tailles disponibles | Normes de production |
|---|---|---|---|
| Barres/tiges | Barres rondes, barres carrées | Diamètre : 0,25″ – 6,0″ (6,35 mm – 152,4 mm) | ASTM A732, AMS 5759 |
| Plaques/Feuilles | Plaques, Feuilles | Épaisseur : 0,025″ – 1,000″ (0,64 mm – 25,4 mm) | ASTM A732, AMS 5537 |
| Fils | Fils | Diamètre : 0,010″ – 0,250″ (0,25 mm – 6,35 mm) | ASTM A580, AMS 5832 |
| Tubes/Tuyaux | Tubes, Tuyaux | Diamètre extérieur : 0,250″ – 6,000″ (6,35 mm – 152,4 mm) | ASTM A732, AMS 5759 |
Soudage et transformation
UNS R30400 and T-400C offer good weldability and machinability:
- Soudage: Peut être soudé en utilisant des méthodes standard telles que le soudage TIG et MIG avec un préchauffage et un traitement thermique post-soudage appropriés.
- Traitement: Usinables à l'aide d'outils en carbure, bien que des précautions soient nécessaires en raison de leur dureté et de leur ténacité élevées.
Avantages et inconvénients
| Aspect | Détails |
|---|---|
| Avantages | Résistance à l'usure exceptionnelle, résistance et dureté élevées, bonne résistance à la corrosion et adéquation aux applications à haute température. |
| Désavantages | Coût plus élevé par rapport aux matériaux conventionnels, nécessite une expertise en manipulation en raison de leur haute résistance et dureté. |
Alliages similaires
| Nom de l'alliage | Comparaison |
|---|---|
| États-Unis R30006 | Teneur en cobalt plus élevée, offrant une résistance à l'usure et une dureté supérieures à celles du Tribaloy T-400 et T-400C. |
Comparaison d'alliages similaires
| Propriété/caractéristique | UNS R30400/T-400C | États-Unis R30006 |
|---|---|---|
| Teneur en cobalt (%) | 60.0 | 60.0 |
| Teneur en chrome (%) | 30.0 | 28.0 |
| Teneur en nickel (%) | 5.0 | 4.0 |
| Teneur en molybdène (%) | 5.0 | 1.0 |
| Dureté, Rockwell C (HRC) | 40 – 48 | 38 – 45 |
| Applications | Automotive, Aerospace, Oil & Gas | Outils industriels, composants d'usure |
This detailed article provides a comprehensive introduction to UNS R30400 and T-400C alloys, highlighting their chemical composition, mechanical properties, performance characteristics, industry applications, available forms and sizes, production standards, welding and processing capabilities, as well as advantages, disadvantages, and comparisons with similar alloys. Engineers and professionals seeking high-performance materials for applications demanding wear resistance, strength, and reliability will find this information valuable for selecting the appropriate alloy to meet their specific needs.