Product Specification: LION® R30605 (Haynes 25 / L-605 Type)
LION® R30605 is a high-performance, solid-solution strengthened cobalt-base alloy. Known in the industry as Haynes 25 or L-605, it is the strongest of the fabricable cobalt alloys. It combines excellent high-temperature strength with superior resistance to oxidation, sulfidation, and metal galling.
1. Temel Teknik Özellikler
- High-Temp Strength: Maintains exceptional mechanical properties for long-term service up to 980°C (1800°F).
- Sulfidation Resistance: Superior resistance to sulfur-bearing atmospheres compared to standard nickel alloys.
- Excellent Galling Resistance: Proven performance in metal-on-metal wear applications, such as high-temperature bearings.
- Non-Magnetic: Remains non-magnetic even after severe cold working.
2. Teknik Özellikler (Nominal Kompozisyon)
| Öğe | Sembol | Ağırlık %'si (Tipik) |
|---|---|---|
| Kobalt | ortak | Denge |
| Tungsten | W | 14.0 – 16.0% |
| Krom | CR | 19.0 – 21.0% |
| Nikel | İçinde | 9.0 – 11.0% |
| Manganese | Mn | 1.0 – 2.0% |
| Ütü | Fe | ≤ %3,0 |
3. Mechanical Properties (Annealed Condition)
- Nihai Çekme Dayanımı: ≥ 860 MPa (125 ksi)
- 0.2% Yield Strength: ≥ 310 MPa (45 ksi)
- Uzama: ≥ 30%
- Sertlik: ≤ 277 HB (Standard Annealed)
Endüstri Çapraz Referansı: UNS R30605 | AMS 5537 | AMS 5759 | Haynes 25 / L-605 Type.
Data verified against Haynes International and ASTM F90 metallurgical standards.