Product Specification: LION® R30605 (Haynes 25 / L-605 Type)
LION® R30605 is a high-performance, solid-solution strengthened cobalt-base alloy. Known in the industry as Haynes 25 or L-605, it is the strongest of the fabricable cobalt alloys. It combines excellent high-temperature strength with superior resistance to oxidation, sulfidation, and metal galling.
1. 主要技術特點
- High-Temp Strength: Maintains exceptional mechanical properties for long-term service up to 980°C (1800°F).
- Sulfidation Resistance: Superior resistance to sulfur-bearing atmospheres compared to standard nickel alloys.
- Excellent Galling Resistance: Proven performance in metal-on-metal wear applications, such as high-temperature bearings.
- Non-Magnetic: Remains non-magnetic even after severe cold working.
2. 技術規格（標稱成分）
| 元素 | 象徵 | 重量%（典型值） |
|---|---|---|
| 鈷 | 鈷 | 平衡 |
| Tungsten | 瓦 | 14.0 – 16.0% |
| 鉻 | 鉻 | 19.0 – 21.0% |
| 鎳 | 在 | 9.0 – 11.0% |
| Manganese | 錳 | 1.0 – 2.0% |
| 鐵 | 鐵 | ≤3.0% |
3. Mechanical Properties (Annealed Condition)
- 極限拉伸強度： ≥ 860 MPa (125 ksi)
- 0.2% Yield Strength: ≥ 310 MPa (45 ksi)
- 伸長： ≥ 30%
- 硬度： ≤ 277 HB (Standard Annealed)
產業交叉參考： UNS R30605 | AMS 5537 | AMS 5759 | Haynes 25 / L-605 Type.
Data verified against Haynes International and ASTM F90 metallurgical standards.