Tribaloy™ T-900 Alloy: Product Introduction
Tribaloy™ T-900 is a high-performance cobalt-based alloy renowned for its exceptional wear resistance, high temperature strength, and corrosion resistance. This article provides a detailed introduction to Tribaloy™ T-900, covering its chemical composition, mechanical properties, performance at different temperatures, industry applications, shapes and sizes, production standards, welding and processing capabilities, advantages and disadvantages, and a comparison with similar alloys.
Kimyasal bileşim
Tribaloy™ T-900 has a sophisticated chemical composition designed for superior performance in demanding environments:
| Öğe | Kompozisyon (%) |
|---|---|
| Kobalt (Co) | 52.0 – 60.0 |
| Krom (Cr) | 26.0 – 32.0 |
| Nikel (Ni) | 10.0 – 12.0 |
| Molibden (Mo) | 6.0 – 8.0 |
| Volfram (W) | 3.0 – 5.0 |
| Karbon (C) | 00,05 – 0,15 |
| Demir (Fe) | 1.0 – 3.0 |
| Silikon (Si) | Maksimum 1,0 |
| Manganez (Mn) | Maksimum 1,0 |
| Fosfor (P) | 00,04 maksimum |
| Kükürt (S) | 00,04 maksimum |
Mekanik özellikler
Tribaloy™ T-900 exhibits excellent mechanical properties suitable for high-stress applications:
| Mülk | Değer |
|---|---|
| Çekme Dayanımı, ksi (MPa) | 175 (1205) dk |
| Akma Dayanımı (%0,2 ofset), ksi (MPa) | 140 (965) dk |
| Uzama (2 inç cinsinden) | 10 min |
| Sertlik, Rockwell C (HRC) | 38 – 46 |
Performans Özellikleri
Tribaloy™ T-900 offers outstanding performance across various conditions:
- Aşınma Direnci: Superior resistance to abrasion, erosion, and galling, making it ideal for components subjected to extreme wear conditions.
- Yüksek Sıcaklık Dayanımı: Maintains excellent strength and hardness at elevated temperatures, up to approximately 1100°F (593°C).
- Korozyon Direnci: Asitler ve alkaliler dahil agresif ortamlarda oksidasyona ve korozyona karşı iyi direnç.
Endüstri Uygulamaları
Tribaloy™ T-900 is utilized in industries requiring superior wear and corrosion resistance:
| Sanayi Sektörü | Uygulamalar |
|---|---|
| Otomotiv | Valf bileşenleri, piston segmanları ve turboşarj yatakları. |
| Havacılık | Uçak motorlarındaki rulmanlar, contalar ve türbin bileşenleri. |
| Petrol ve Gaz | Sondaj ekipmanındaki matkap uçları, pompa bileşenleri ve valf yuvaları. |
Şekiller ve boyutlar
Tribaloy™ T-900 is available in various forms and sizes to meet diverse application needs:
- Formlar: Levhalar, levhalar, çubuklar, tüpler ve özel şekiller.
- Boyutlar: Kalınlığı 0,025 inç ila 1,000 inç (0,64 mm ila 25,4 mm) arasında değişirken çapı 0,25 inç ila 6,0 inç (6,35 mm ila 152,4 mm) arasında değişir.
Üretim Standartları
Tribaloy™ T-900 adheres to stringent production standards ensuring quality and performance:
| Ürün Formu | Mevcut Şekiller | Mevcut Boyutlar | Üretim Standartları |
|---|---|---|---|
| Çubuklar/Çubuklar | Yuvarlak çubuklar, kare çubuklar | Çap: 0,25″ – 6,0″ (6,35mm – 152,4mm) | ASTM A732, AMS 5759 |
| Plakalar/Levhalar | Plakalar, Çarşaflar | Kalınlık: 0,025″ – 1,000″ (0,64mm – 25,4mm) | ASTM A732, AMS 5537 |
| Teller | Teller | Çap: 0,010″ – 0,250″ (0,25mm – 6,35mm) | ASTM A580, AMS 5832 |
| Tüpler/Borular | Tüpler, Borular | Dış Çap: 0,250″ – 6,000″ (6,35mm – 152,4mm) | ASTM A732, AMS 5759 |
Kaynak ve İşleme
Tribaloy™ T-900 offers good weldability and machinability:
- Kaynak: Uygun ön ısıtma ve kaynak sonrası ısıl işlemle TIG ve MIG kaynağı gibi standart yöntemler kullanılarak kaynak yapılabilir.
- İşleme: Machinable using carbide tools, though care is required due to its high hardness and toughness.
Avantajlar ve dezavantajlar
| Bakış açısı | Detaylar |
|---|---|
| Avantajları | Exceptional wear and corrosion resistance, high strength and hardness, reliability in harsh environments. |
| Dezavantajları | Geleneksel malzemelere göre maliyetinin yüksek olması, yüksek mukavemeti ve sertliği nedeniyle kullanımında uzmanlık gerektirmektedir. |
Benzer Alaşımlar
| Alaşım Adı | Karşılaştırmak |
|---|---|
| Stellitler 6 | Higher cobalt content, offering superior wear resistance and hardness compared to Tribaloy™ T-900. |
Benzer Alaşımların Karşılaştırılması
| Özellik/Özellik | Tribaloy™ T-900 | Stellitler 6 |
|---|---|---|
| Kobalt İçeriği (%) | 52.0 – 60.0 | 60.0 |
| Krom İçeriği (%) | 26.0 – 32.0 | 28.0 |
| Nikel İçeriği (%) | 10.0 – 12.0 | 4.0 |
| Molibden İçeriği (%) | 6.0 – 8.0 | 1.0 |
| Sertlik, Rockwell C (HRC) | 38 – 46 | 38 – 45 |
| Uygulamalar | Automotive, Aerospace, Oil & Gas | Endüstriyel aletler, aşınma bileşenleri |
This detailed article provides a comprehensive introduction to Tribaloy™ T-900 alloy, highlighting its chemical composition, mechanical properties, performance characteristics, industry applications, available forms and sizes, production standards, welding and processing capabilities, as well as advantages, disadvantages, and comparisons with similar alloys. Engineers and professionals seeking durable materials for applications demanding wear resistance, high strength, and reliability will find this information valuable for selecting the appropriate alloy to meet their specific needs.