Tribaloy™ T-900 Alloy: Product Introduction
Tribaloy™ T-900 is a high-performance cobalt-based alloy renowned for its exceptional wear resistance, high temperature strength, and corrosion resistance. This article provides a detailed introduction to Tribaloy™ T-900, covering its chemical composition, mechanical properties, performance at different temperatures, industry applications, shapes and sizes, production standards, welding and processing capabilities, advantages and disadvantages, and a comparison with similar alloys.
Composición química
Tribaloy™ T-900 has a sophisticated chemical composition designed for superior performance in demanding environments:
| Elemento | Composición (%) |
|---|---|
| Cobalto (Co) | 52.0 – 60.0 |
| Cromo (Cr) | 26.0 – 32.0 |
| Níquel (Ni) | 10.0 – 12.0 |
| Molibdeno (Mo) | 6,0 – 8,0 |
| Tungsteno (W) | 3,0 – 5,0 |
| Carbono (C) | 0.05 – 0.15 |
| Hierro (Fe) | 1.0 – 3.0 |
| Silicio (Si) | 1,0 máx. |
| Manganeso (Mn) | 1,0 máx. |
| Fósforo (P) | 0.04 max |
| Azufre (S) | 0.04 max |
Propiedades mecánicas
Tribaloy™ T-900 exhibits excellent mechanical properties suitable for high-stress applications:
| Propiedad | Valor |
|---|---|
| Resistencia a la tracción, ksi (MPa) | 175 (1205) minutos |
| Límite elástico (0,2 % de compensación), ksi (MPa) | 140 (965) min |
| Alargamiento (% en 2 pulgadas) | 10 min |
| Dureza, Rockwell C (HRC) | 38 – 46 |
Características de presentación
Tribaloy™ T-900 offers outstanding performance across various conditions:
- Resistencia al desgaste: Superior resistance to abrasion, erosion, and galling, making it ideal for components subjected to extreme wear conditions.
- Resistencia a altas temperaturas: Maintains excellent strength and hardness at elevated temperatures, up to approximately 1100°F (593°C).
- Resistencia a la corrosión: Buena resistencia a la oxidación y corrosión en ambientes agresivos, incluidos ácidos y álcalis.
Aplicaciones industriales
Tribaloy™ T-900 is utilized in industries requiring superior wear and corrosion resistance:
| Sector industrial | Aplicaciones |
|---|---|
| Automotor | Componentes de válvulas, aros de pistón y cojinetes de turbocompresor. |
| Aeroespacial | Cojinetes, sellos y componentes de turbinas en motores de aeronaves. |
| Petróleo y gas | Brocas, componentes de bombas y asientos de válvulas en equipos de perforación. |
Formas y tamaños
Tribaloy™ T-900 is available in various forms and sizes to meet diverse application needs:
- Formas: Láminas, placas, barras, tubos y formas personalizadas.
- Tamaños: Espesor que varía de 0,025 pulgadas a 1,000 pulgadas (0,64 mm a 25,4 mm), diámetro que varía de 0,25 pulgadas a 6,0 pulgadas (6,35 mm a 152,4 mm).
Estándares de producción
Tribaloy™ T-900 adheres to stringent production standards ensuring quality and performance:
| Formulario de producto | Formas disponibles | Tamaños disponibles | Estándares de producción |
|---|---|---|---|
| Barras/varillas | Barras redondas, barras cuadradas | Diámetro: 0,25″ – 6,0″ (6,35 mm – 152,4 mm) | ASTM A732, AMS 5759 |
| Platos/Hojas | Platos, Hojas | Espesor: 0,025″ – 1,000″ (0,64 mm – 25,4 mm) | ASTM A732, AMS 5537 |
| alambres | alambres | Diámetro: 0,010″ – 0,250″ (0,25 mm – 6,35 mm) | ASTM A580, AMS 5832 |
| Tubos/Tuberías | Tubos, Tuberías | Diámetro exterior: 0,250″ – 6,000″ (6,35 mm – 152,4 mm) | ASTM A732, AMS 5759 |
Soldadura y procesamiento
Tribaloy™ T-900 offers good weldability and machinability:
- Soldadura: Se puede soldar mediante métodos estándar como soldadura TIG y MIG con un precalentamiento adecuado y un tratamiento térmico posterior a la soldadura.
- Procesando: Machinable using carbide tools, though care is required due to its high hardness and toughness.
Ventajas y desventajas
| Aspecto | Detalles |
|---|---|
| Ventajas | Exceptional wear and corrosion resistance, high strength and hardness, reliability in harsh environments. |
| Desventajas | De mayor coste respecto a los materiales convencionales, requiere experiencia en su manipulación debido a su alta resistencia y dureza. |
Aleaciones similares
| Nombre de la aleación | Comparación |
|---|---|
| Estelitas 6 | Higher cobalt content, offering superior wear resistance and hardness compared to Tribaloy™ T-900. |
Comparación de aleaciones similares
| Propiedad/Característica | Tribaloy™ T-900 | Estelitas 6 |
|---|---|---|
| Contenido de cobalto (%) | 52.0 – 60.0 | 60.0 |
| Contenido de cromo (%) | 26.0 – 32.0 | 28.0 |
| Contenido de níquel (%) | 10.0 – 12.0 | 4.0 |
| Contenido de molibdeno (%) | 6,0 – 8,0 | 1.0 |
| Dureza, Rockwell C (HRC) | 38 – 46 | 38 – 45 |
| Aplicaciones | Automotive, Aerospace, Oil & Gas | Herramientas industriales, componentes de desgaste. |
This detailed article provides a comprehensive introduction to Tribaloy™ T-900 alloy, highlighting its chemical composition, mechanical properties, performance characteristics, industry applications, available forms and sizes, production standards, welding and processing capabilities, as well as advantages, disadvantages, and comparisons with similar alloys. Engineers and professionals seeking durable materials for applications demanding wear resistance, high strength, and reliability will find this information valuable for selecting the appropriate alloy to meet their specific needs.