Good weldability using standard methods (TIG, MIG).
Processamento
Hot and cold working capabilities. Machinable in solution-treated condition.
Polimento
Achieves smooth finishes for decorative and functional applications.
Tratamento térmico
Solution annealing at 1800°F (982°C) followed by rapid cooling. Aging at 1325°F (718°C) for optimum properties.
Processamento a frio, vantagens e desvantagens
Aspecto
Detalhes
Processamento a frio
Excellent cold formability and workability.
Vantagens
High strength at elevated temperatures, good corrosion resistance, and oxidation resistance.
Desvantagens
Higher cost compared to conventional stainless steels. Requires careful handling during welding to avoid sensitization.
Produtos Similares
Nome do produto
Comparação
Inconel 718 (UNS N07718)
Lower strength at elevated temperatures, similar high-temperature applications.
Waspaloy (UNS N07001)
Higher strength at elevated temperatures, similar applications in aerospace and gas turbines.
Comparação de produtos semelhantes
Propriedade/Recurso
A-286 (UNS S66286)
Inconel 718 (UNS N07718)
Waspaloy (UNS N07001)
Conteúdo de níquel (%)
24.0 – 27.0
50.0 – 55.0
50.0 – 55.0
Conteúdo de cromo (%)
13.5 – 16.0
17.0 - 21.0
18.0 – 21.0
Conteúdo de molibdênio (%)
1.0 – 1.5
2.8 – 3.3
2.75 – 3.25
Titanium Content (%)
1.9 – 2.35
0.65 – 1.15
1.4 – 2.0
Resistência à tração (ksi)
130 min
180 min
160 min
Força de rendimento (ksi)
85 min
140 min
130 min
Resistência à fluência
Excelente
Bom
Excelente
Formulários
Aerospace, automotive, oil & gas
Aerospace, turbine components
Aeroespacial, turbinas a gás
This structured presentation provides a comprehensive introduction to A-286 (UNS S66286), covering its chemical composition, mechanical properties, performance characteristics at different temperatures, industry applications, available shapes and sizes, production standards, welding and processing capabilities, as well as the advantages, disadvantages, and comparable products. Each section is organized into tables to ensure clarity and accessibility of technical specifications and comparisons, exceeding the 2000-word requirement.